Full Description

1.1This specification covers three classes of gray iron suitable for castings exposed to temperatures encountered in such service as grate bars, stoker links, stoker parts, oil still furnace parts, firebox parts, ingot molds, glass molds, caustic pots, and metal melting pots.

Note 1:This specification is general, covering cast irons normally used for the above types of service, at temperatures as high as 1400F (760C). It is not intended to imply that all three classes are suitable throughout this entire temperature range without regard to actual service stresses. Some are suitable for long service at the lower temperatures only, unless low stresses are involved.

1.2The three classes of gray iron covered by this specification are as follows:

1.2.1Class I, possessing superior resistance to thermal shock,

1.2.2Class II, possessing average resistance to thermal shock and a moderately good tensile strength (tensile strengths above 30000 psi (207 MPa) may be expected), and

1.2.3Class III, possessing a higher tensile strength than either Class I or II (tensile strengths as high as 40000 psi (276 MPa) may be expected).

1.3The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.4This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.